Résistance de puce de précision à film mince de nitrure de tantale - Série TAR
TAR Series1206 ±0.05% 50 1/2W Series13KΩ 5K/Reel

Taille	Tolérance	TCR (ppm /℃)	Puissance	Résistance (Ohm)	Emballage
1206	±0.05%	50	1/2W	13K	5K/Reel

Caractéristiques environnementales

Item	Requirement	Test Method
Temperature Coefficient of Resistance (T.C.R.)	As Spec.	JIS-C-5201-1 4.8 IEC-60115-1 4.8 -55°C ~ + 125°C, 25°C is the reference temperature
Short Time Overload	ΔR±0.1%	JIS-C-5201-1 4.13 RCWV x 2.5 or Max. Overload Voltage whichever is lower for 5 seconds
Insulation Resistance	>1000 MΩ	JIS-C-5201-1 4.6 IEC-60115-1 4.6 Max. Apply 100VDC for 1 minute
Operational Life	ΔR±0.1%	MIL-STD-202 Method 108 Condition D Steady State TA=125°C at derated power. Measurement at 24±4 hours after test conclusion.
Biased Humidity	ΔR±0.1%	MIL-STD-202 Method 103 1000 hrs 85°C/85%RH 10% of operating power.
High Temperature Exposure	ΔR±0.15%	MIL-STD-202 Method 108 at + 155°C for 1000 hrs
Board Flex	ΔR±0.1%	JIS-C5201-1 4.23 Bending 2mm for 60 seconds
Solderability	95% min. coverage	JIS-C-5201-1 4.17 IEC-60115-1 4.17 245 ± 5°C for 3 seconds
Resistance to Soldering Heat	ΔR±0.1%	JIS-C-5201-1 4.18 IEC-60115-1 4.18 260 ± 5°C for 10 seconds
Endurance	ΔR±0.1%	IEC-60115-1 4.25 1000 +48/-0 hours, loaded with RCWV or Vmax in chamber controller 85± 2°C, 1.5 hours on and 0.5 hours off
Moisture Resistance	ΔR±0.1%	MIL-STD-202 Method 106 65 ± 2°C, 80~100%RH, 10 CYCLES, 24 hours/cycle
Temperature Cycling	ΔR±0.1% for 125°C	JESD22 Method JA-104 -55°C to + 125°C, 1000 cycles -55°C to + 155°C, 1000 cycles
Temperature Cycling	ΔR±0.2% for 155°C
Mechanical Shock	ΔR±0.1%	MIL-STD-202 Method 213 Wave Form: Tolerance for half sine shock pulse. Peak value is 100g's. Normal duration (D) is 6.
Vibration	ΔR±0.1%	MIL-STD-202 Method 204 5 g's for 20 min., 12 cycles each of 3 orientations, 10-2000 Hz
ESD	ΔR±0.1%	AEC-Q200-002 Human body model TAR02, TAR03: 0.2KV TAR05, TAR06: 1KV
Resistance to Solvents	Marking unsmeared	MIL-STD-202 Method 215 Add Aqueous wash chemical - OKEM Clean or equivalent. Do not use banned solvents.
Terminal Strength	No broken	AEC-Q200-006 Force of 1kg for 60 seconds.
Flammability	No ignition of the tissue paper or scorching or the pinewood board	UL-94 V-0 or V-1 are acceptable. Electrical test not required.
Sulfur Test	ΔR±1%	EIA-977(Conditions B) 105 ± 2°C, no power rating for 750 hrs

RCWV (Rated Continuous Working Voltage)=√(P x R) or Max. Operating Voltage whichever is lower.
☑ Storage Temperature: 15 ~ 28°C; Humidity < 80%RH

Condition de soudage

IR Reflow Soldering / Wave Soldering (Flow Soldering)

(1) Time of IR reflow soldering at maximum temperature point 260°C：10s
(2) Time of wave soldering at maximum temperature point 260°C：10s
(3) Time of soldering iron at maximum temperature point 410°C：5s

Marquage

Marking Table

Code	E96	Code	E96	Code	E96	Code	E96
01	100	25	178	49	316	73	562
02	102	26	182	50	324	74	576
03	105	27	187	51	332	75	590
04	107	28	191	52	340	76	604
05	110	29	196	53	348	77	619
06	113	30	200	54	357	78	634
07	115	31	205	55	365	79	649
08	118	32	210	56	374	80	665
09	121	33	215	57	383	81	681
10	124	34	221	58	392	82	698
11	127	35	226	59	402	83	715
12	130	36	232	60	412	84	732
13	133	37	237	61	422	85	750
14	137	38	243	62	432	86	768
15	140	39	249	63	442	87	787
16	143	40	255	64	453	88	806
17	147	41	261	65	464	89	825
18	150	42	267	66	475	90	845
19	154	43	274	67	487	91	866
20	158	44	280	68	499	92	887
21	162	45	287	69	511	93	909
22	165	46	294	70	523	94	931
23	169	47	301	71	536	95	953
24	174	48	309	72	549	96	976

Code	A	B	C	D	E	F	G	H	X	Y	Z
Multiplier	10s⁰	10¹	10²	10³	10⁴	10⁵	10⁶	10⁷	10^-1	10^-2	10^-3

0603 3digit marking for E24
Example: 101=100Ω 102=1KΩ

E24

0805~1206 4digit marking
Example

Resistance	100Ω	2.2KΩ	10KΩ	49.9KΩ	100KΩ
marking	1000	2201	1002	4992	1003

Emballage

Packing Quantity & Reel Specifications (Unit :mm)

Type	ØA	ØB	ØC	W	T	Paper Type(EA)	Emboss Plastic Tape(EA)
TAR02	178.0±1.0	60.0+1.0	13.5±0.7	9.5±1.0	11.5±1.0	10,000	-
TAR03	178.0±1.0	60.0+1.0	13.5±0.7	9.5±1.0	11.5±1.0	5,000	-
TAR05	178.0±1.0	60.0+1.0	13.5±0.7	9.5±1.0	11.5±1.0	5,000	-
TAR06	178.0±1.0	60.0+1.0	13.5±0.7	9.5±1.0	11.5±1.0	5,000	-

Paper Tape Specifications

Type	A	B	W	E	F	P0	P1	P2	ΦD₀	T
TAR02	0.70±0.05	1.16±0.05	8.00±0.10	1.75±0.05	3.5±0.05	4.00±0.10	2.00±0.05	2.00±0.05	1.55±0.05	0.40±0.03
TAR03	1.10±0.05	1.90±0.05	8.00±0.10	1.75±0.05	3.5±0.05	4.00±0.10	4.00±0.10	2.00±0.05	1.55±0.05	0.60±0.03
TAR05	1.60±0.05	2.37±0.05	8.00±0.10	1.75±0.05	3.5±0.05	4.00±0.10	4.00±0.10	2.00±0.05	1.55±0.05	0.75±0.05
TAR06	2.00±0.05	3.55±0.05	8.00±0.10	1.75±0.05	3.5±0.05	4.00±0.10	4.00±0.10	2.00±0.05	1.55±0.05	0.75±0.05

☑ Peel force of top cover tape
☑ The peel speed shall be about 300mm/min±5%
☑ The peel force of top cover tape shall be between 8gf to 60gf

Code

1302

Téléchargement de fichiers

Fiche technique

Résistance de puce de précision à film mince de nitrure de tantale - Série TAR

Étiquette
résistances métalliques

CHERCHER

Recherche conditionnelle: Recherche croisée

Meilleure Vente

Résistance de précision à couche mince en nitrure de tantale (Série TAR TAR06ATDU1302) Fabricant - Viking

Basée à Taïwan, Viking Tech Corporation est l'un des principaux fabricants de Résistance de précision à couche mince en nitrure de tantale (Série TAR TAR06ATDU1302) depuis 1997.Et leurs produits sont utilisés dans toute l'industrie automobile, les applications de dispositifs électroniques, avec une tolérance de fabrication allant jusqu'à 0,01 % et un TCR allant jusqu'à 2 ppm dans une large gamme de tailles de boîtiers.

TS16949/ ISO9001/ ISO14001 et répondant aux normes AEC-Q200, Viking propose des résistances de précision anti-soufre, anti-surtension, à impulsion, haute tension, haute puissance, y compris des résistances à film mince/épais, des résistances automobiles, des résistances MELF, des résistances de détection de courant, etc. Inducteurs à faible bruit, faible TC, haute puissance tels que les inducteurs RF, les inducteurs de puce, les inducteurs de puissance, les inducteurs variables, les inducteurs à puce en ferrite, les inducteurs blindés, les inducteurs à bobine et les inducteurs à immersion.

Résistance de précision à couche mince en nitrure de tantale (Série TAR TAR06ATDU1302)Viking propose aux clients des résistances de puissance, des inductances de puissance et des condensateurs électrolytiques en aluminium de haute qualité, bénéficiant d'une solide réputation. Grâce à une technologie avancée et à 25 ans d'expérience, Viking s'assure de répondre aux exigences de chaque client.

Découvrez nos produits de qualité Inducteur de puissance, Résistance de puce à film mince, Inducteur RF, Résistance CMS, Résistance de détection de courant, film métallique, résistances métalliques, Résistance à film épais, Condensateur CMS, Résistance de puissance et n'hésitez pas à Nous contacter.

Produit Principal

APPLICATIONS AUTOMOBILES

Résistance de précision en film mince 0,01 %, TC2ppm, wirebondale, anti-corrosion, MELF. Détection...

APPLICATIONS MÉDICALES

Inducteurs céramiques haute fréquence, de petite taille jusqu'à 01005. Film mince, multicouche, bobiné,...

APPLICATIONS DE COMMUNICATION

Le condensateur céramique multicouche offre une haute tension, haute fréquence, faible bruit, haute...

Résistance de précision à couche mince en nitrure de tantale (Série TAR TAR06ATDU1302)Fabricants - Viking

Résistance de précision à couche mince en nitrure de tantale (Série TAR TAR06ATDU1302)